Analysis of resistance to fatigue between straight solid and anatomic abutments of Morse taper system / Análise da resistência à fadiga entre pilares retos e anatômicos do sistema cone Morse

Background: The study of the phenomenon of fatigue is essential because implant failures usually are caused by this process. Purpose: The objective of this study was to examine the fatigue resistance of straight and anatomical abutments joints that were submitted to cyclic loads. Material and method: We used 37 Morse taper implants and 37 abutments, divided into two groups (n= 16: straight abutment, n= 21 anatomical abutment). The sets were submitted to cyclic loading (5 million) using servo-hydraulic equipment. Three sets from each group were subjected to bending tests to determine the maximum load resistance, which served as the parameter for comparison of the cyclic tests. We evaluated number of cycles, load and bending moment. Result: Of the 31 abutments cyclically tested, 17 (54.8%) fractured in fewer than 5 million cycles; 8 (25.8%) of these were straight abutments, and 9 (29%) were anatomical. A total of 14 samples (45.2%) resisted the cyclic loading. According to Fisher's exact test, there was no difference between groups as the fracture. Conclusion: Despite of the straight abutments have higher average load and bending moment on the anatomical, both types of abutments showed similar performance as the fracture strength in vitro.

Contexto: O estudo do fenômeno de fadiga é essencial porque as falhas de implantes geralmente são causadas por este processo. Objetivo: O objetivo deste estudo foi analisar a resistência à fadiga de conjuntos de pilares retos e anatômicos que foram submetidos a cargas cíclicas. Material e método: Foram utilizados 37 implantes cone Morse e 37 pilares, divididos em dois grupos (n = 16: pilares retos, n = 21: pilares anatômicos). Os conjuntos foram submetidos à carga cíclica (5.000.000) usando o equipamento servo-hidráulico. Três conjuntos de cada grupo foram submetidos a testes de flexão para determinar a resistência de carga máxima, o que serviu de parâmetro para comparação dos testes cíclicos. Foram avaliados número de ciclos, carga e momento de flexão. Resultado: Dos 31 pilares ciclicamente testados, 17 (54,8%) fraturaram em menos de 5 milhões de ciclos; 8 (25,8%) destes eram pilares retos, e 9 (29%) eram anatômicos. Um total de 14 amostras (45,2%) resistiu à carga cíclica. De acordo com o teste exato de Fisher, não houve diferença entre os grupos quanto à fratura. Conclusão: Apesar dos pilares retos terem maior carga média e momento de flexão que os anatômicos, os dois tipos de pilares apresentaram desempenho semelhante quanto a resistência à fratura in vitro.

Análise da resistência à fratura entre pilares retos e angulados do sistema cone Morse / Analysis of resistance to fracture between straight and angled abutments of Morse taper system

Objetivo: Analisar a resistência à fratura por fadiga dos conjuntos implante-pilar, nos tipos reto e angulado, submetidos a cargas cíclicas similares às mastigatórias. Material e método: Foram utilizados 32 implantes (3,75 × 11 mm) com sistema cone Morse e 32 pilares, separados em dois grupos: pilares retos e angulados (n=16) (Neodent, Curitiba, PR, Brasil). Os conjuntos foram submetidos a testes cíclicos em equipamento servo-hidráulico, fixando-se o número de ciclos em cinco milhões. Foram avaliados: número de ciclos, carga e momento de força das amostras. O Teste de Fisher e o Teste ANOVA foram aplicados (p<0,005). Amostras fraturadas foram analisadas em microscopia eletrônica de varredura (MEV). Resultado: Dos pilares retos, quatro resistiram ao número de ciclos estabelecidos, suportando cargas entre 470 N e 510 N. No grupo dos angulados, nove amostras resistiram a cargas entre 570 N e 890 N. Quanto às amostras fraturadas abaixo do número de ciclos, no grupo pilar reto, nove fraturaram com cargas entre 470 N e 630 N. No grupo pilar angulado, cinco amostras fraturaram com cargas entre 760 N e 890 N. Foi calculado, para cada conjunto implante-pilar, o momento de força (Médias: Grupo reto - 4.335,2 Nmm, Grupo angulado - 3.923,3 Nmm). Conclusão: Os dois tipos de pilares (retos e angulados), em condições in vitro, comportaram-se estatisticamente de forma semelhante, sendo aceita a hipótese nula de que não há diferença de resistência à fratura entre os grupos.

Objective: The aim of this study was to verify the fatigue fracture resistance of the implant-abutment joint, in straight and angled types, subject to cyclic loads similar to chewing. Material and method: It was used 32 implants system (3.75 × 11mm) with Morse taper and 32 abutment, divided in two groups: abutment straight and angled (n = 16) (Neodent, Curitiba, PR, Brazil). The sets were submitted to cyclic testing using servo-hydraulic equipment, fixing the number of cycles at 5 million. It was evaluated the number of cycles, load and moment force of the samples. The Fisher test and ANOVA were applied (p<0,005). Fractured samples were analyzed in the scanning electron microscopy (SEM). Result: Straight abutment, four resisted the cycles number established, supporting loads between 470N and 510N. Angled abutment: nine resisted to loads between 570N and 890N. Regarding the fractured samples below the number of cycles, in the straight abutment, nine fractured with loads between 470N and 630N. In the angled abutment, five fractured with loads ranging from 760N and 890N. The moment of the force was calculated for each joint implant-abutment (Averages: Straight Group - 4335,23Nmm, angled Group - 3923,37Nmm). Conclusion: Two types of abutments (straight and angled), in vitro conditions, statistically behaved similarly, and accepts the null hypothesis that there is no difference in fracture resistance between groups. .

Dentin deproteinization effect on bond strength of self-adhesive resin cements

This study examined the effect of deproteinization on the bond strength between self-adhesive resin cements and dentin surfaces that were untreated (control), acid-etched, or acid-etched and subjected to a post-etch deproteinization treatment. Cylinders of RelyX Unicem or BisCem (n = 6) cement were build-up on the dentin surfaces and tested to determine shear strength. The results were analyzed using two-way ANOVA and Tukey's test (5%). While neither dentin pretreatment improved the bond strength for RelyX Unicem, deproteinization treatments resulted in greater bond strength in BisCem specimens while acid etching alone did not improve the performance of the material.

Influência da marca do condicionador ácido na resistência de união da resina composta à dentina / Influence of acid etchant brand on bond strength of composite resin to dentin

Introdução: Apesar da importância da etapa de condicionamento ácido nos procedimentos adesivos, pouco se sabe sobre o efeito da marca do condicionador ácido sobre a união do adesivo à dentina. Objetivo: Este estudo avaliou o efeito de diferentes condicionadores ácidos na união da resina composta à dentina. Material e Método: Vinte e cinco incisivos bovinos tiveram a coroa dividida em duas hemissecções. As superfícies vestibulares foram desgastadas com lixa carbeto de silício (SiC) #180 até a exposição de dentina, seguida por lixas SiC #600 para padronização da smear layer. As amostras foram aleatoriamente alocadas em cinco grupos (n = 10), de acordo com marca do condicionador ácido: 3M ESPE, Ultradent, Dentsply, Villevie e DFL. Apenas um sistema de união convencional de dois passos (Ambar, FGM) foi utilizado. Matrizes de silicone foram utilizadas na confecção de três cilindros de resina composta em cada amostra. Após 24 horas, os cilindros foram testados sob carga de cisalhamento até a falha. Os dados foram analisados com ANOVA a um critério e teste de Tukey (α = 0,05). O modo de falha foi avaliado em microscopia óptica e os dados submetidos ao Teste Qui-quadrado (α = 0,05). Resultado: Não houve diferença estatística na resistência de união obtida entre os condicionadores ácidos avaliados. Houve predomínio de falhas adesivas, exceto para os condicionadores da Dentsply e DFL, que demonstraram similaridade entre falhas adesivas e mistas. Conclusão: As diferentes marcas de condicionadores ácidos avaliados não influenciaram a resistência de união de resina composta à dentina.

Introduction: Despite the importance of the acid etching step on bonding procedures, little is known about the acid etchant brand effect on bond strength of adhesive to dentin. Objective: The aim of this study was to evaluate the effect of different acid etchants at the bond strength of composite resin to dentine. Material and Method: Twenty five bovine incisors had their crown sectioned in two hemi-sections. The buccal surfaces were grounded with #180 silicon carbide (SiC) abrasive paper to exposure of dentin, followed by #600 SiC paper to standardize the smear layer. The samples were randomly allocated into five groups (n = 10) according to acid etchant brands: 3M ESPE, Ultradent, Dentsply, Villevie and DFL.Only a two-step etch-and-rinse adhesive system (Ambar, FGM) was used. Silicon molds were used to build-up three resin composite cylinder per sample. After 24 hours, cylinders were submitted to shear load until the failure. Data were analyzed by one way ANOVA and Tukey`s test (α = 0,05). The failure mode was evaluated under optical microscopy and the data were submitted to Chi-square test (α = 0,05). Result: There was no statistical difference on bond strength obtained between the acid etchants evaluated. There was predominance of adhesive failures, except for etchants of Dentsply and DFL that showed similarity between mixed and adhesive failures. Conclusion: Different brands of acid etchants did not influence on the bond strength of composite resin to dentin.